Effect of film blowing process on film properties

2021-03-27  1885

Blown film technology

The process flow of blown film is plasticizing and extruding material to form tube blank, which is inflated, cooled, pulled and coiled. In the process of blown film forming, according to the different extrusion and traction directions, it can be divided into three kinds: flat extrusion up blowing method, flat extrusion down blowing method and flat extrusion flat blowing method.

1. Flat extrusion and top blowing

In this method, a right angle die is used, that is, the discharge direction of the die is perpendicular to the extruder, the extruded tube billet is pulled up to a certain distance, and then it is clamped by a herringbone plate. The extruded tube is inflated into a foam tube by the compressed air introduced from the bottom, and its transverse dimension is controlled by the amount of compressed air, and the longitudinal dimension is controlled by the traction speed. The blown thin foam tube can be obtained by cooling and shaping Membrane.

Due to the tenacity and stable traction of the foam hanging on the top of the membrane tube, it can produce a wide range of thickness and wide film, so it is most widely used. The main plastic varieties suitable for up blowing method are PVC, PE, PS and HDPE, especially the wide film of PVC and PE.

2. Flat extrusion blow down method

Down blowing method has a good cooling effect because the tube billet is pulled downward, and the film is drawn into the traction roll by self weight, so the operation of film drawing is more convenient. However, the installation of the machine is too high, and the film bubble is hung on the plastic section which has not been cooled and shaped. When the pulling speed is fast or the production of thick film and the material density is large, it is easy to break the tube film PP, PA, PVDC (vinylidene chloride) and other high crystallinity plastics, to reduce the crystallinity by quenching.

3. Flat extrusion and flat blowing

This method uses a straight die concentric with the screw of the extruder, and the foam pipe and the center line of the die are on the same horizontal plane, which is called flat extrusion and flat blowing method. This method is only suitable for blowing small diameter film products, such as LDPE, PVC, PS film. The flat blowing method is also suitable for the production of blown heat shrinkable films.

Main process factors affecting blown film

There are many factors that affect the stability of blown film processing. Understanding these factors is conducive to the control of the production process, and also to improve the physical and mechanical properties and appearance quality of the film.

1. Temperature control

Temperature control is a key link in film production, which directly affects the product quality. There are two kinds of temperature control conditions: one is that the temperature gradually rises from the charging section of the fuselage to the exit of the nose; the other is that the temperature of the middle and front sections of the fuselage is the highest, and the temperature of the nose is lower. For the equipment with small aspect ratio, especially the transparency, the second method is used. The selection of temperature in each section of the main engine is related to the materials used. If the extruder with diameter of 65 mm, length diameter ratio of 20:1 and compression ratio of 3:1 is used to produce PE film, the temperature control is as follows: feeding section 140-150 ℃, middle section 170-180 ℃, front section 180-190 ℃ and die head 180 ℃.

2. Expansion and traction of membrane tube

The molten material is extruded from the die head to form a cylindrical tube blank. At the same time, air is introduced into the die to inflate the film blank into a film bubble. The formation of the film bubble makes the melt stretch and thin, and combines with the stretch caused by the traction effect to form a biaxial tensile film. In order to prepare films with equal longitudinal and transverse strength, it is required that the transverse blowing ratio (the ratio of the bubble diameter to the die diameter) and the longitudinal drafting ratio (the ratio of the linear velocity of the drawn film tube to that of the non drawn film tube) should be the same. In the actual production, the die with the same specification is often used to make films with different thickness and width by adjusting the blowing ratio and traction ratio.

The blow up ratio is usually controlled at 1.5-3. If the blow up ratio is too small, the transverse strength is low; if the blow up ratio is too large, the process stability, film forming and production continuity are low. The draft ratio is generally controlled between 3 and 7. In production practice, the draft ratio is determined when the film thickness, blowing ratio and film gap are determined. Therefore, adjusting the draft ratio is a way to adjust the film thickness. In order to reduce the film thickness, the traction speed can be increased, that is, the draft ratio should be increased, but the film tube should be prevented from being broken when the draft ratio is too large.

3. Cooling and setting

The cooling of film tube is very important. It should be air-cooled immediately after blowing. If the air cooling is not good, the film will stick and cannot be lifted, or they will stick to each other under the pressure of traction roller. Therefore, the cooling effect and cooling rate will directly affect the quality and output of products. The common cooling method is to use compressed air to blow directly around the membrane bubble through the wind ring. In order to improve the cooling effect, cooling air, secondary air ring, mandrel inner cooling and other technologies are also used.


免费无码婬片69视频软件 | 国产精品久久久久久无码欧美内衣 | 又爽又色一级毛片免费观看 | 国产日韩精品无码区免费专区国产 | 欧美性猛交XXXX乱大交3未删减版 | 麻豆一区一区三区四区 | 中文字幕在线观看一区二区 | 国产美女在线自卫福利姬 | 免费无遮挡无码永久在线观看视频 | 一本大道之高清乱伦视频 | 国产亚无精久久久久久无码 | 欧美蜜桃91传媒大学生 | 亚洲色婷婷综合久久二区 | 女人扒开腿婬乱A片 | 亚洲精品乱码久久久久久蜜桃91 | 国产原创成人视频网站 | 国产伦精品一区二区三区视频黑人 | 西西888WWW大胆无码 | 小辣椒成人A级视频www | 日韩精品中文字幕一区二区三区 | 91大神大课约女教师在线观看 | 成人免费视频中文字幕 | 人人差人人爽人人干 | 中文字幕免费网站 | 永久免费看成人AV的动态图 | 中文字幕乱码第三页 | 91精品久久久久久久久无码果冻 | 久久精品国产999大香线蕉 | 国产乱人乱偷精品视频 | 少妇做爰全过程免费视频 | 国产精品91一区二区 | 女女蕾丝边一区二区三区国产 | 免费 无码 国产在线53 | 国产情侣自拍伊人 | 黑人亚洲精品A片久久99 | 一区二区在线免费观看 | 特级BBBBBBBBB视频 | 亚洲国产日产无码精品蜜 | 中文字幕在线观看视频一区 | 熟女老阿V8888AV | 操逼喷水疯狂视频91 |